The Phenomenon of High Hardness Values on the S-Phase Layer of Austenitic Stainless Steel via Screen Plasma Nitriding Process

Kim, Sang-Gweon and Yeo, Kook-Hyun and Cho, Yong-Ki and Lee, Jae-Hoon and Okumiya, Masahiro (2018) The Phenomenon of High Hardness Values on the S-Phase Layer of Austenitic Stainless Steel via Screen Plasma Nitriding Process. Advances in Materials Physics and Chemistry, 08 (06). pp. 257-268. ISSN 2162-531X

[thumbnail of AMPC_2018062811481296.pdf] Text
AMPC_2018062811481296.pdf - Published Version

Download (6MB)

Abstract

The purpose of this study is to improve the surface properties of austenitic stainless steel using the double-folded electrode screen plasma nitriding (SPN) process. In general, the S-phase is well-known for its excellent properties such as improved hardness and wear resistance along with sustained corrosion resistance. The concentrated nitrogen via SPN process was injected to form S-phase with time at 713 K. This study was carried out under the conditions of 44 at% of nitrogen injection, which was higher than 25 at% known as the condition of no precipitation of S-phase formed by the SPN process, and 20 K higher than the maximum temperature without precipitation phase. The hardness analysis of stainless steel sample treated by the SPN process at 713 K showed a much higher value than the typical nitriding hardness at a depth of lower nitrogen than the maximum nitrogen concentration. The SPN 20 hr treated specimen showed the average value of 2339 HV while 40 hr showed the average value of 2215 HV. The result is attributed to the concentrated nitrogen formed in the SPN process reacting with the alloying elements contained in the base material to form fine precipitates, thus producing a synergy effect of the extreme hardening effect; that is, the movement of precipitates and dislocations due to the GP-zone (Guinier-Preston zone).

Item Type: Article
Subjects: Archive Digital > Chemical Science
Depositing User: Unnamed user with email support@archivedigit.com
Date Deposited: 30 Mar 2023 09:04
Last Modified: 30 Dec 2023 13:38
URI: http://eprints.ditdo.in/id/eprint/444

Actions (login required)

View Item
View Item